VERIFICATION #13aThin film result
Thin film calculation result. Recall that you can choose from multiple substrate materials such as silicon, GaAs, or InP and from deposition materials such as gold or silver.
Input string: 59.348,2.3,0
101.11,1.35,0
59.348,2.3,0
101.11,1.35,0
59.348,2.3,0
Total number of films entered: 5 Incident angle: 30 degrees Index of ambient material(n,k)=1 Material of substrate: silicon Units for thickness and wavelength should be nm.
Nomenclature is as follows: perp refers to s-polarization ; para refers to p polarization ; mag means magnitude.
The following are the field and power, as well as the phase shift for both polarization states. Both reflected and transmitted values are given.
References:
[1] Born and Wolf, Principles of Optics, 7th ed. Chapter 1
[2] Steve Byrnes, http://sbyrnes321.byethost11.com/
ACKNOWLEDGEMENT: Luxpop would like to thank (i) Steve Byrnes of Berkeley for his valuable assistance in correcting previous errors, and (ii) Didier Dutartre for his contribution.
lambda (nm)
mag r_perp (field)
R_perp (power)
mag r_para (field)
R_para (power)
delta r_phase perp
delta r_phase para
mag t_perp (field)
T_perp (power)
mag t_para (field)
T_para (power)
delta t_phase perp
delta t_phase para
897
0.1573
0.02473
0.1214
0.01475
1.088
-2.768
0.4829
0.97527
0.4854
0.98525
-1.373
-1.504
927
0.0357
0.00127
0.0918
0.00843
-0.465
2.218
0.4895
0.99873
0.4878
0.99157
-1.598
-1.699
957
0.1417
0.02007
0.1579
0.02492
-1.970
1.390
0.4857
0.97993
0.4845
0.97508
-1.803
-1.878
987
0.2543
0.06468
0.2348
0.05515
-2.254
1.029
0.4752
0.93532
0.4777
0.94485
-1.985
-2.040
1017
0.3456
0.11947
0.3021
0.09125
-2.440
0.801
0.4618
0.88053
0.4691
0.90875
-2.145
-2.185
1047
0.4173
0.17414
0.3575
0.12780
-2.587
0.628
0.4478
0.82586
0.4602
0.87220
-2.285
-2.315
1077
0.4727
0.22343
0.4021
0.16165
-2.710
0.485
0.4348
0.77657
0.4518
0.83835
-2.407
-2.432
1107
0.5152
0.26539
0.4374
0.19130
-2.816
0.363
0.4234
0.73461
0.4443
0.80870
-2.515
-2.538
1137
0.5475
0.29981
0.4650
0.21624
-2.909
0.256
0.4139
0.70019
0.4379
0.78376
-2.612
-2.635
1167
0.5720
0.32724
0.4863
0.23652
-2.992
0.160
0.4061
0.67276
0.4327
0.76348
-2.699
-2.724
1197
0.5903
0.34851
0.5024
0.25245
-3.067
0.072
0.4001
0.65149
0.4286
0.74755
-2.779
-2.806